Talc Porcelain Granulating Powder Series

Feedstock ready to press for uniaxial and isostatic pressing for the production of oxide ceramic bodies such as grinding media, insulating and wear-resistant parts, etc.

Spray-Dried Alumina Granules for dry pressing and isostatic pressing

Feedstock ready to press for uniaxial and isostatic pressing for the production of oxide ceramic bodies such as grinding media, insulating and wear-resistant parts, etc.

HS1	HS2	HS3	HS4
Bulk Density g/cm3	≥0.8
moisture %	≤0.3;0.5±0.1;0.7±0.1
Particle size distribution 目	60-300;中心径160;140
angle of repose ℃	≤30
Green body density g/cm3 ③	1.75-1.90
loss on ignition%	＜9.0
average shrinkage % ③	17-18
Sintering temperature ℃ ②	1280±10	1330±10	1280±10	1330±10
hold time H	1.0
Porcelain density g/cm3	≥2.85	≥2.85	≈3.0	≈3.0
Porcelain	White	White	black	grayish yellow
Scope of application	Electronic component shell, high frequency ceramic parts		Structural Porcelain

The above data are all measured under experimental conditionsφ22mm weight 10g pressure 80MPa.

Die oben genannten Werte sind nur als Richtwerte zu verstehen und nicht etwa als zugesicherte Eigenschaften. The above mentioned values should be taken only as indications and not as guaranteed properties.

Jiyuan Gengxin Porcelain Co.,LTD

Add: Henan jiyuan city science and technology industrial park

Tel: +86-0391-6634900

Fax: +86-0391-6634922

E-mail: jygx@jygx.com

PREVIOUS：Al2O3 wear-resistant ceramic granulation powder series No next